Humao Gansu Black/Green Silicon for Steel Making

• Customization: Available
• After-sales Service: 24 H
• Color: Black
• Model NO.: HMSIC1
• Application: Refractory, Metallurgy, Chemical, Ceramic, Casting
• Province: Gansu
• Characteristic1: High Hardness
• Characteristic2: Low Expansion Coefficient
• Characteristic3: Good Thermal Conductivity
• Transport Package: Bags
• Specification: 0-10mm, 1-10mm, 0-15mm
• Trademark: HUAMAO
• Origin: China
• HS Code: 28492000
• Production Capacity: 2000000tons/Year

Product Description

Company Profile

 

Product Description

 

At present, in China's foundry industry, the use of induction furnace as cast iron smelting equipment foundries are increasing, however, in the smelting process of silicon carbide is very few, can make it play a full role less, our company research modified silicon carbide can improve the metallurgical quality of molten iron, reduce the oxidation of molten iron. In the process of smelting cast iron with intermediate frequency furnace, the accompanying problems such as poor nodularization, less graphite balls, large use of nodularizing agent, more supercooled graphite in gray iron castings, A-type graphite can not meet customer requirements, and processing difficulties follow. This product can effectively improve the metallurgical quality of molten iron, thereby reducing the above problems.The hardness of silicon carbide is second only to diamond, and it has strong wear resistance. It is an ideal material for wear-resistant pipes, impellers, pump chambers, cyclones, and hopper linings. Its wear resistance is 5 times longer than that of cast iron and rubber. --20 times&def is also one of the ideal materials for aviation runways.
Features:
1. Increase the graphite nucleation core and enhance the graphite nucleation ability. Reduce the subcooling degree of molten iron and reduce the tendency of castings to white.
2. Good deoxidation effect, purify molten iron.
3. Extend the service life of the furnace lining.
4. Reduce the supercooled graphite in gray cast iron and promote the generation of A-type graphite.
5. Adding to ductile iron production can increase the number of graphite balls, improve the nodularization rate, make the graphite balls more round and small, and reduce the amount of nodularizing agent.

Physic Properties
Color	Green
Crystal form	Polygon
Mohs hardness	9.2-9.6
Micro hardness	2840~3320kg/mm²
Melting point	1723
Maximum operating temperature	1600
True density	3.21g/cm³
Bulk density	2.30g/cm³